Effect of phosphogypsum on saline-alkalinity and aggregate stability of bauxite residue

A column experiment was conducted to investigate the effect of phosphogypsum (PG) on the saline- alkalinity, and aggregate stability of bauxite residue. Results showed that: with increasing leaching time, the concentrations of saline-alkali ions decreased while the concentration increased in bauxite residue leachate; compared with CK (control group) treatment, pH, electric conductivity (EC), exchangeable sodium percentage (ESP), sodium absorption ratio (SAR), and exchangeable Na⁺ content of bauxite residue were reduced following PG treatment; average particle sizes in aggregates following CK and PG treatments were determined to be 155 and 193 nm, respectively. SR-μCT test results also confirmed that bauxite residue following PG treatment acquired larger aggregates and larger pore diameter. These results indicate that the PG treatment could significantly modulate the saline-alkalinity, and simultaneously enhance aggregate stability of bauxite residue, which provides a facile approach to reclaim bauxite residue disposal areas.     

The surface carboxyl group of carbonaceous microspheres effects on the synthesis and structure of SiOC ceramics

In this study, C/SiOC and C/SiO₂ composites were prepared by using carbonaceous microspheres with different surface functional groups. Carbonaceous microspheres based on hydrothermal reaction of glucose contains hydroxyl group, while the surface carboxyl group increases after NaOH etching. The hydroxyl group increases the oxygen-enriched structural units of SiOC ceramics, and the C spheres are closely enwrapped in SiOC matrix after pyrolysis at 900 °C. However, the interfacial reaction of surface carboxyl with Si–OH results in the formation of cristobalite SiO₂, and C spheres are not only encased inside the SiOC matrix, but also dispersed outside of SiOC ceramics. After removal of C via calcination at 500 °C for 5 h, C/SiOC and C/SiO₂ composites are transformed into amorphous SiO₂ and cristobalite SiO₂, respectively. The thermogravimetric analysis indicates the oxidation resistance of SiOC is superior to that of C and SiO₂.     

Tests of a Two-Stage Core at the KV-1 Test Facility: Physical Aspects and Results

Atomic Energy - The physical aspects and main results of reactor tests of a two-stage core consisting of fresh fuel assemblies and a significant number of fuel assemblies from the previous core,...     

功能性小麦品种的概念、类别和发展前景（网络首发、推荐阅读）

结合全球倡导的营养导向型农业和功能性食品的内容，首次提出“功能性小麦品种”的概念，将其定义为“含有对人体健康有益的活性成分，可调节人体有益代谢，能给人体健康带来某种益处或满足特定人群的特殊需求，同时可以作为日常食物的口感正常、无毒副作用的小麦品种类型”；结合疫情警示和我国进入后工业时代后，人们需求必将由“吃得饱”、“吃得好”向“吃得健康”转变，因而提出继高产品种、优质品种之后培育“功能性小麦品种”的育种目标。根据多年关于小麦淀粉、蛋白、酯类和其他成分的功能研究结果，介绍新育成的“麦黄酮”、“高色素”、“高抗性淀粉”、“富锌”、“低醇溶蛋白”和“低植酸”等功能性小麦新品种（系）的营养特性和农艺产量状况；根据“健康中国2030”规划等国家战略，进行“功能性品种培育是解决我国功能性食品‘卡脖子’的关键基础，一种功能性品种可以形成一类功能性食品，多种功能性品种可以形成我国功能性面制品产业，推动我国整个食品工业的发展”的前景展望；根据功能性品种及其食品的稳定性和可靠性是产品和市场的“生命线”，从对消费者负责的高度，提出关于“功能性农作物品种审定导向和组建功能性成分检测机构；编制有关功能性品种和食品的国家或行业标准，设立功能性食品和功能性农作物品种的商业标志，保证我国功能性农作物品种及其食品健康发展”等方面的具体建议。     

Adsorption of the IFKhAN-92 Inhibitor on Chromium–Nickel Steel from Mineral Acid Solutions

Protection of Metals and Physical Chemistry of Surfaces - Impedance spectroscopy was used to study the adsorption of the IFKhAN-92 inhibitor, a triazole derivative, on cathodically polarized...     

Effects of Different Short-Term UV-B Radiation Intensities on Metabolic Characteristics of Porphyra haitanensis

The effects of ultraviolet (UV) radiation, particularly UV-B on algae, have become an important issue as human-caused depletion of the protecting ozone layer has been reported. In this study, the effects of different short-term UV-B radiation on the growth, physiology, and metabolism of Porphyra haitanensis were examined. The growth of P. haitanensis decreased, and the bleaching phenomenon occurred in the thalli. The contents of total amino acids, soluble sugar, total protein, and mycosporine-like amino acids (MAAs) increased under different UV-B radiation intensities. The metabolic profiles of P. haitanensis differed between the control and UV-B radiation-treated groups. Most of the differential metabolites in P. haitanensis were significantly upregulated under UV-B exposure. Short-term enhanced UV-B irradiation significantly affected amino acid metabolism, carbohydrate metabolism, glutathione metabolism, and phenylpropane biosynthesis. The contents of phenylalanine, tyrosine, threonine, and serine were increased, suggesting that amino acid metabolism can promote the synthesis of UV-absorbing substances (such as phenols and MAAs) by providing precursor substances. The contents of sucrose, D-glucose-6-phosphate, and beta-D-fructose-6-phosphate were increased, suggesting that carbohydrate metabolism contributes to maintain energy supply for metabolic activity in response to UV-B exposure. Meanwhile, dehydroascorbic acid (DHA) was also significantly upregulated, denoting effective activation of the antioxidant system. To some extent, these results provide metabolic insights into the adaptive response mechanism of P. haitanensis to short-term enhanced UV-B radiation.     

Optimization of room-temperature TCR of polycrystalline La0.9-xSrxK0.1MnO3 ceramics by Sr adjustment

High-density La_0.9-xSr_xK_0.1MnO₃ ceramics (LSKMO, A-site = La, Sr and K, 0 ≤ x ≤ 0.25) are successfully fabricated by using facile sol-gel method. Electrical properties are performed by using combination of phenomenological percolation (PP) model, double exchange (DE) mechanism, and Jahn-Teller (JT) effect. Moreover, X-ray diffraction and scanning electron microscopy are employed to analyze the structure and morphology of LSKMO ceramics. Valence states and ionic stoichiometry are assessed by using X-ray photoemission spectrometry. Results reveal that Sr²⁺ ions, substituting La³⁺ ions, significantly influenced DE mechanism and JT effect. In addition, Sr-doping plays essential role in improving electrical properties of LSKMO ceramics. At optimal doping content of x = 0.09, peak temperature coefficient of resistance (TCR) of the resistivity is found to be 11.56% K^?1 at 297.15 K, which is optimal TCR for A-site K-occupied perovskite manganese oxides. These results confirm that polycrystalline LSKMO ceramics render high room-temperature TCR values due to Sr-doping.     

Microstructure and electric properties of Pr-doped Pb(Zr0.52Ti0.48)O3 ceramics

Improving the piezoelectric activity of lead zirconate titanate (PZT) ceramics is of great importance for practical applications. In this study, the influence of Pr³⁺ doping on the ferroelectric phase composition, microstructure, and electric properties on the A-site of (Pb_1-1.5xPr_x)(Zr_0.52Ti_0.48)O₃ is extensively investigated. A dense and fine microstructural sample is obtained with the introduction of Pr³⁺. The results show that the morphotropic phase boundary (MPB) moves to the rhombohedral phase region. The rhombohedral and tetragonal phases exhibit an ideal coexistence in the 4 mol.% Pr³⁺ doped (PPZT4) samples. Lead vacancy and the reduction of the potential energy barrier are considered to be the key mechanisms for donor doping, which is upheld by the Pr³⁺ doping. Combining the I-E hysteresis loops with the P-E hysteresis loops, it becomes apparent that both contribution maximums of the domain switching and residual polarisation are in PPZT4. Moreover, the thermal aging resistance of PZT is improved by doping, and the temperature stability is optimised from 83% in PZT to 96% in PPZT4. Hence, an appropriate amount of Pr³⁺ doping can effectively improve the piezoelectric activity of PZT ceramics in the MPB area and optimise the performance stability of the material under application temperatures.     

Freeze-drying and mechanical redispersion of aqueous PEDOT:PSS

Poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) films are attracting famous applications in antistatic coating, energy storage and conversion, printed electronics, and biomedical fields due to their conductivity, optical transparency and flexibility. However, PEDOT:PSS has poor dispersion stability during long-term storage and transport. Moreover, the dried PEDOT:PSS films are insoluble in any solvent and cannot be redispersed again. In comparison to bake drying, here, a feasible strategy to achieve mechanically redispersed PEDOT:PSS with the help of freeze-drying process was reported. The redispersed PEDOT:PSS can recover not only the initial characters such as pH, chemical composition, viscosity, and particle size under similar solid contents, but also conductivity and surface morphology of treated films. In addition, the treated film exhibits self-healing properties similar to pristine film in terms of mechanical and electrical properties. This technology enables reuse and overcomes the technical problems of PEDOT:PSS dispersion, realizing real-time processing to meet variable applications.     

Development of vibration damping materials based on butyl rubber: A study of the phase equilibrium,rheological, and dynamic properties of compositions

A detailed study of butyl rubber-based vibration damping formulations linking their composition, morphology, phase structure, viscosity, mechanical loss factor, and other characteristics is presented for the first time. High performance of the compositions including aromatic petroleum oil is explained by limited solubility of the plasticizer that leads to the formation of a highly-viscous emulsion (η_20°C ≈ 1000 Pa·s) consisting of a swollen butyl rubber matrix and dispersed oil droplets in the broad composition range. Chalk is found to be the best inorganic filler as its spherical particles provide strong adhesion to the reinforcing layer of aluminum foil. Aiming to eliminate ecologically unfriendly aromatic compounds, a new low-cost binding agent formulation based on butyl rubber mixed with polyisobutylene and highly refined mineral oil is suggested. Being environmentally safe, it possesses high viscosity of 1000–3000 Pa·s, cohesion strength of 3.5–5.0 N/cm, penetration of 4.5–6.0 mm, and mechanical loss factor up to 0.34 at room temperature, which are as good as, or even better than, the properties of currently produced vibration damping materials containing aromatic compounds. New materials can be used in car and aircraft parts for effective vibration isolation.